EVA Hot melt adhesive 280.10

EVA hot melt adhesive for edgebanding·unfilled



For automatic edgbanders, for instance for bonding edgebands of HPL/CPL,
poylester, resinated paper, solid wood and veneer. If thermoplastic
edgebands are to be bonded, the special properties of the edgebands and
the reverse primer application have to be tested before use.
May be used for the applications straight edges, softforming and BAZ.

Directions for use:

High heat resistance, good adhesion, long open time, high hot tack. Excellent
resistance to oxidation as well as good colour stability in the melt. Very good
mechanical processing characteristics, accurate application without hot melt
The structure of the edge materials and the processing conditions will
influence the processes of joining and bonding. Customer trials before use
are recommended. The materials to be used must be free of grease and dust
and be dry, they also have to match perfectly. Wood moisture content should
be at 8 - 10 %. Minimum temperature of substrates and ambient air should
not be below 18 °C. Avoid draught.


Technical Data:
Density[g/cm3]:  approx. 1.03
Softening range: approx. 100 (Kofler bench)
Appearance: final digit 0 = light beige : 1 = white




Preliminary cleaning while hot by scraping with a spatula. Remove any
residues when cold with Jowat® Cleaner 402.40.


May be stored for 12 months after date of delivery ex production site, cool
and dry.

Packaging:  Granulate; types of packaging and units upon request.

For further information concerning handling, transport and disposal, please
refer to the Material Safety Data Sheet.
Our information on this data sheet is based on test results from our
laboratories as well as on experience gained in the field by our customers. It
can, however, not cover all parameters for each specific application and is
therefore not binding for us. The information given in this leaflet represents
neither a performance guarantee nor a guarantee of properties, nature,
condition, state or quality. No liability may be derived from these indications
nor from the recommendations made by our free technical advisory service.